PERMABOND TA4610
Harmonization Code : 3907.30.00.40 | Epoxy Mold Compounds containing by weight more than 70 % silicon dioxide
Main features
- Underwater Structural Bonding
- Primer-Free Polyolefin Assembly
- Microparticle-Controlled 1 mm Gaps
Product Description
Permabond TA4610 is a two-part, 1:1 toughened acrylic adhesive for polypropylene, polyethylene, metals, composites, and dissimilar-material assemblies. It bonds low-surface-energy plastics without primer or surface treatment and supports water-resistant and underwater bonding. The thixotropic system contains microparticles for a maximum 1 mm gap. At 23 deg C, typical pot life is 5 to 8 minutes, fixture strength develops in 12 to 15 minutes, and handling strength in 40 to 50 minutes. Working strength develops in 6 to 8 hours, with cured shear strengths of 15 N/mm^2 on HDPE and 13 N/mm^2 on epoxy FRP.
Key features
- Underwater Bonding Capability: Supports underwater bonding and water-resistant assemblies.
- Primer-Free PP and PE: Bonds polypropylene and polyethylene without primer or surface treatment.
- Microparticle Gap Control: Microparticles provide 1 mm maximum gap control for assembled joints.
Applications
Applications include underwater or water-resistant bonding, polypropylene and polyethylene assembly, and bonding metals, composites, and dissimilar substrates.
TDS, SDS & Technical Documents
Technical Specifications
General Properties
Other Properties
Curing Conditions
Additional Information
As-supplied / before-processing properties
Values identify the separate Part A and Part B components or the mixed adhesive, as stated.
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Part A viscosity | 200,000 to 500,000 | mPa s | At 25 deg C; thixotropic |
| Part B viscosity | 20,000 to 30,000 | mPa s | At 25 deg C |
| Specific gravity | 1.0 | Part A and Part B | |
| Mix ratio | 1:1 | Part A to Part B | |
| Maximum gap fill | 1 | mm | Contains microparticles for gap control |
| Pot life | 5 to 8 | minutes | 2 g + 2 g at 23 deg C |
| Fixture time | 12 to 15 | minutes | 0.1 N/mm^2 shear strength at 23 deg C |
| Handling time | 40 to 50 | minutes | 0.3 N/mm^2 shear strength at 23 deg C |
After-processing / final-state properties
Strength values are typical cured results for the listed substrate combinations.
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Shear strength - polypropylene | 8 | N/mm^2 | Typical; substrate failure observed |
| Shear strength - polyethylene | 7 | N/mm^2 | Typical; substrate failure observed |
| Shear strength - HDPE | 15 | N/mm^2 | Typical |
| Shear strength - mild steel to PP | 7 | N/mm^2 | Typical |
| Shear strength - stainless steel to PP | 5 | N/mm^2 | Typical |
| Shear strength - aluminum to PP | 4 | N/mm^2 | Typical |
| Shear strength - carbon fiber | 8 | N/mm^2 | Typical |
| Shear strength - epoxy FRP | 13 | N/mm^2 | Typical |