PERMABOND TA4592
Harmonization Code : 3907.30.00.40 | Epoxy Mold Compounds containing by weight more than 70 % silicon dioxide
Main features
- External-Mix Automated Dispensing
- Sub-30-Second Gel Time
- Motor Magnet and Ferrite Bonding
Product Description
Permabond TA4592 is a two-component, 1:1 external-mix structural acrylic adhesive for bonding magnets and ferrites in electric motors. Part A and Part B are dispensed separately and mixed as the beads fall onto the part, supporting high-speed automated assembly without a static mixer. The system fills gaps up to 1 mm, gels in less than 30 seconds, fixtures zinc in 10-30 seconds, and cures fully in 24 hours. Typical cured performance includes 20-25 N/mm2 shear strength on mild steel, 15-20 N/mm2 on zinc, and 10-20 kJ/m2 impact strength.
Key features
- External-Mix Automation: Two dispensed components mix in air without a static mixer.
- Sub-30-Second Gel: A 1 g plus 1 g mix gels in less than 30 seconds.
- Motor Magnet and Ferrite Bonding: Targets magnet and ferrite attachment in electric-motor assembly.
Applications
Applications include automated bonding of magnets and ferrites in electric motors and supported structural acrylic assemblies.
TDS, SDS & Technical Documents
Technical Specifications
General Properties
Other Properties
Curing Conditions
Thermal Properties
Additional Information
As supplied / before processing
Part A and Part B are shown separately; processing values apply to the stated 1:1 external-mix system.
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Appearance | Part A: blue; Part B: yellow-green | As supplied | |
| Part A viscosity | 10,000-15,000; 40,000-60,000 | mPa s | 20 rpm; 2.5 rpm at 25 deg C |
| Part B viscosity | 5,000-6,000; 12,000-15,000 | mPa s | 20 rpm; 2.5 rpm at 25 deg C |
| Density | Part A: 1.1; Part B: 1.1 | As supplied | |
| Mix ratio | 1:1 | External mix | |
| Maximum gap fill | 1 | mm | Typical curing property |
| Cure milestones | Gel: <30 seconds; zinc fixture: 10-30 seconds; full cure: 24 hours | Gel based on 1 g Part A plus 1 g Part B | |
| Storage temperature | 2 to 7 | deg C | Recommended storage range |
After processing / final state
Values are typical for cured adhesive and the stated substrates, cure periods, and methods.
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Shear strength - mild steel | 20-25 | N/mm2 | Typical cured value |
| Shear strength - zinc | 15-20 | N/mm2 | Typical cured value |
| Shear strength - steel to ferrite, 3 minutes | 4 | N/mm2 | Typical cure development |
| Shear strength - steel to ferrite, 24 hours | >14 | N/mm2 | Substrate failure |
| Tensile strength | 25 | N/mm2 | ASTM D2095 |
| Impact strength | 10-20 | kJ/m2 | ASTM D-950 |
| Coefficient of thermal expansion | 80 x 10^-6 | 1/K | ASTM D-696 |
| Thermal conductivity | 0.1 | W/(m K) | ASTM C-177 |