PERMABOND ET502
Harmonization Code : 3214.10.00 | Putty and other mastics | Resin cements, caulking compounds and other mastics
Main features
- Clear Two-Part Epoxy Bondline
- 5-10 Minute Handling Strength
- 4 mm Gap Filling
Product Description
Permabond ET502 is a colorless two-part epoxy adhesive for general-purpose bonding where a clear bondline and room-temperature cure are required. The 1:1 system has a mixed viscosity of 45,000-90,000 mPa s at 25 deg C, fills gaps up to 4 mm, and provides a 3-5 minute pot life at 23 deg C. Handling strength is reached in 5-10 minutes, with full cure after 24 hours at 23 deg C. Applications include wood, metals, ceramics, selected plastics, and composites.
Key features
- Clear Bondline: Colorless components cure to a clear epoxy bondline.
- Rapid Handling: Reaches handling strength in 5-10 minutes at 23 deg C.
- 4 mm Gap Fill: Fills bond gaps up to 4 mm with a 1:1 mix ratio.
Applications
Applications include general-purpose bonding of wood, metals, ceramics, selected plastics, and composites where a clear bondline is required.
TDS, SDS & Technical Documents
Technical Specifications
General Properties
Other Properties
Mechanical Properties
Thermal Properties
Electrical Properties
Additional Information
As supplied / before processing
Part A and Part B values are shown separately; mixed values apply after the stated 1:1 ratio.
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Appearance | Part A: colorless; Part B: colorless | As supplied | |
| Part A viscosity | 80,000-150,000 | mPa s | At 25 deg C |
| Part B viscosity | 10,000-25,000 | mPa s | At 25 deg C |
| Mixed viscosity | 45,000-90,000 | mPa s | At 25 deg C |
| Specific gravity | Part A: 1.2; Part B: 1.1 | As supplied | |
| Mix ratio | 1:1 | By volume | |
| Maximum gap fill | 4 | mm | Typical curing property |
| Usable / pot life | 3-5 | minutes | At 23 deg C |
After processing / final state
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Shear strength - mild steel | 8-12 | N/mm2 | ISO 4587 |
| Peel strength - aluminum | 5-20 | N/25 mm | ISO 4578 |
| Hardness | 70-80 | Shore D | ISO 868 |
| Elongation at break | <5 | % | ISO 37 |
| Glass transition temperature, Tg | 40-50 | deg C | Typical cured value |
| Dielectric strength | 15-25 | kV/mm | Typical cured value |